Investigations on magnetic and semiconducting nanomaterials prepared by sol-gel and electrospinning routes

dc.contributor.authorDas, Arnab Kumar
dc.date.accessioned2019-07-23T06:58:00Z
dc.date.accessioned2023-10-26T09:55:49Z
dc.date.available2019-07-23T06:58:00Z
dc.date.available2023-10-26T09:55:49Z
dc.date.issued2018
dc.descriptionSupervisor: A. Srinivasanen_US
dc.description.abstract1-d undoped, ferromagnetic Co doped and non-magnetic Mg doped ZnO nanowires consisting of interconnected nanometer sized beads have been prepared by electrospinning method. Annealed as-spun undoped 1-d ZnO exhibited the highest ever achieved TC of 885 K. Maximum magnetization of 0.039 emu/g was observed for 500 C annealed sample at an applied field of 10 kOe. The observed room temperature ferromagnetism (RTFM) is due to singly ionized oxygen vacancies in undoped 1-d ZnO. Although no magnetization was observed in Mg doped 1-d ZnO, considerable enhancement in band gap energy was observed upon Mg2+ doping. Mg doping quenched the oxygen defects in 1-d ZnO. However, Co doped 1-d ZnO exhibited RTFM. Defects analysis revealed that exchange interaction between local spin-polarized electrons and conduction electrons of Co is responsible for RTFM in these nanostructures. Moreover, Zn vacancies present in the samples decreased upon increasing Co doping. 0-d and 1-d CaFe2O4 nanostructures have been prepared by sol-gel and electrospinning routes, respectively. Cubic CaFe2O4 nanoparticles slowly transformed to orthorhombic phase when annealed above 300 C and the transformation completes at 1100 C. Superparamagnetic behavior is associated with the cubic phase and weak ferrimagnetic behaviour was found in the orthorhombic phase. 1100 C annealed orthorhombic 0-d CaFe2O4 exhibited Néel temperature at ~175 K. Co substitution in Ca site in 0-d CaFe2O4 improved its magnetic properties. Phase transformation from cubic to orthorhombic phase was also observed in 0-d Ca0.9Co0.1Fe2O4. 1-d cubic CaFe2O4 also slowly transformed to orthorhombic phase when annealed above 500 C. Apart from clarifying the mechanisms responsible for RTFM in ZnO nanostructures, this work also revealed several new applications for these novel ZnO and CaFe2O4 nanostructures.en_US
dc.identifier.otherROLL NO.11612120
dc.identifier.urihttp://172.17.1.107:4000/handle/123456789/1335
dc.language.isoenen_US
dc.relation.ispartofseriesTH-2007;
dc.subjectPHYSICSen_US
dc.titleInvestigations on magnetic and semiconducting nanomaterials prepared by sol-gel and electrospinning routesen_US
dc.typeThesisen_US
Files
Original bundle
Now showing 1 - 2 of 2
No Thumbnail Available
Name:
Abstract-TH-2007_11612120.pdf
Size:
136.57 KB
Format:
Adobe Portable Document Format
Description:
ABSTRACT
No Thumbnail Available
Name:
TH-2007_11612120.pdf
Size:
4.57 MB
Format:
Adobe Portable Document Format
Description:
THESIS
License bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
license.txt
Size:
1.71 KB
Format:
Plain Text
Description: