Pala, Laxmi Prasad Rao2024-01-302024-01-302024ROLL NO.186107109https://gyan.iitg.ac.in/handle/123456789/2524Supervisor: Peela, Nageswara RaoThe escalating demand for energy from renewable sources, driven by the depletion of fossil resources and environmental concerns, underscores the importance of green energy solutions. Solar energy, an abundant and renewable resource, presents a viable option, since only 0.015% reaching Earth is capable of meeting total global energy demand. While photovoltaic cells convert solar energy to electricity, challenges in storage and distribution necessitate alternative approaches, such as converting solar energy to chemical energy, specifically hydrogen fuel. This study explores solar light utilization for chemical energy generation as a promising avenue to meet contemporary energy needs sustainably. In this study, Titanium dioxide (TiO2) thin films are fabricated using a sol-gel spin coating method, incorporating modifiers and surfactants to control film structure and porosity. Photocatalytic overall water splitting (POWS) is explored as a sustainable solution for renewable hydrogen production. An optofluidic planar microreactor is constructed for photocatalytic water splitting with Pt/TiO2 photocatalyst thin films as photocatalyst. The Pt/TiO2 film with thickness 1650±119 nm showed a highest rate of 16.35 mmol h-1 g-1 (4.7 μmol h-1 cm-2) hydrogen production at an optimum reactant flowrate of 0.3 mL min-1 under visible light irradiation. The stability study carried out for 4 cycles of 5 h each proved that the photocatalyst was stable and the film was well adhered to the glass substrate. Another optofluidic planar microreactor, utilizing IrO2/TiO2 films, is developed for oxygen production through water splitting under visible light. An oxygen evolution rate of 3.99 mmol h-1 g-1 (1.84 μmol h-1 cm-2) was observed from the IrO2/TiO2 film of 3078 ± 362 nm thickness at an optimal flow rate of 0.3 mL min-1 in the presence of visible light. The stability study showed that the IrO2/TiO2 film was stable for at least 4 cycles, indicating the superior activity of the film firmly adhered to the glass substrate. The study culminates in the development of a single semiconductor-based photocatalyst, TiO2, with Pt and IrO2 as co-catalysts for overall water splitting. The 2.5IrO2/0.5Pt/TiO2 photocatalyst exhibits ideal POWS, producing hydrogen and oxygen from pure water under visible and simulated solar light (SSL). The rate of hydrogen and oxygen production were 9.73 and 5.32 μmol g-1 h-1, respectively, with a H2/O2 ratio of 1.82 under SSL with intensity 101.4 mW cm-2. The research provides insights into catalyst properties, scalability, and integrated systems for large-scale hydrogen production, contributing to the advancement of renewable energy and photocatalysis.enTitanium Dioxide Thin FilmSol-gel Spin CoatingPlatinum and Iridium Oxide CocatalystsPhotodepositionOptofluidic Planar MicroreactorHydrogen EvolutionOxygen EvolutionPhotocatalytic overall Water SplittingMethylene Blue DegradationPhotocatalysisThesis